On the measurement of relative powder-bed compaction density in powder-bed additive manufacturing processes
Loading...
Date
2018-10-05
Authors
Ali, Usman
Mahmoodkhani, Yahya
Imani Shahabad, Shahriar
Esmaeilizadeh, Reza
Liravi, Farzad
Sheydaeian, Esmat
Huang, Ke Yin
Marzbanrad, Ehsan
Vlasea, Mihaela
Toyserkani, Ehsan
Advisor
Journal Title
Journal ISSN
Volume Title
Publisher
Elsevier
Abstract
Experimental studies in the literature have identified the powder-bed compaction density as an important parameter, governing the quality of additively manufactured parts. For example, in laser powder-bed fusion (LPBF), the powder-bed compaction density directly affects the effective powder thermal conductivity and consequently the temperature distribution in melt pool. In this study, this physical parameter in a LPBF build compartment is measured using a new methodology. A UV curable polymer is used to bind powder-bed particles at various locations on the powder-bed compartment when Hastelloy X was used. The samples are then scanned using a nano-computing tomography (CT) system at high resolution to obtain an estimation of the relative powder-bed compaction density. It is concluded that due to the interaction between the recoater and the variation in the powder volume accumulated ahead of the recoater across the build compartment, the relative powder-bed compaction density decreases along the recoater moving direction (from 66.4% to 52.4%.). This variation in the powder-bed compaction density affects the density and surface roughness of the final printed parts that is also investigated. Results show that the part density and surface quality decrease ~0.25% and ~20%, respectively, along the build bed in direction of the recoater motion.
Description
The final publication is available at Elsevier via http://dx.doi.org/10.1016/j.matdes.2018.06.030 © 2018. This manuscript version is made available under the CC-BY-NC-ND 4.0 license http://creativecommons.org/licenses/by-nc-nd/4.0/
Keywords
Additive manufacturing, 3D printing, Compaction density, Selective laser melting, Laser powder-bed fusion, Hastelloy X